Ultrasonic Cleaning involves the use of high-frequency sound waves (above the upper range of human hearing, or about 18 kHz) to remove a variety of contaminants from parts immersed in aqueous media. The contaminants can be dirt, oil, grease, buffing/polishing compounds, and mold release agents, just to name a few. Materials that can be cleaned include metals, glass, ceramics, and so on.
Typical applications found in the metals industry are removing chips and cutting oils from cutting and machining operations, removing buffing and polishing compounds prior to plating operations, and cleaning greases and sludge from rebuilt components for automotive and aircraft applications.
Ultrasonic cleaning is powerful enough to remove tough contaminants, yet gentle enough not to damage the substrate. It provides excellent penetration and cleaning in the smallest crevices and between tightly spaced parts in a cleaning tank.
The use of ultrasonics in cleaning has become increasingly popular due to the restrictions on the use of chlorofluorocarbons such as 1,1,1-trichloroethane. Because of these restrictions, many manufacturers and surface treaters are now using immersion cleaning technologies rather than solvent-based vapor degreasing. The use of ultrasonics enables the cleaning of intricately shaped parts with an effectiveness that corresponds to that achieved by vapor degreasing.
In a process termed cavitation, micron-size bubbles form and grow due to alternating positive and negative pressure waves in a solution. The bubbles subjected to these alternating pressure waves continue to grow until they reach resonant size. Just prior to the bubble implosion, there is a tremendous amount of energy stored inside the bubble itself.
Temperature inside a cavitating bubble can be extremely high, with pressures up to 500 atm. The implosion event, when it occurs near a hard surface, changes the bubble into a jet about one-tenth the bubble size, which travels at speeds up to 400 km/hr toward the hard surface. With the combination of pressure, temperature, and velocity, the jet frees contaminants from their bonds with the substrate. Because of the inherently small size of the jet and the relatively large energy, ultrasonic cleaning has the ability to reach into small crevices and remove entrapped soils very effectively.
The ultrasonic generator converts a standard electrical frequency of 60 Hz into the high frequencies required in ultrasonic transmission, generally in the range of 20 to 80 kHz. Many of the better generators today use advanced technologies such as sweep frequency and auto-follow circuitry. Frequency sweep circuitry drives the transducers between a bandwidth slightly greater and slightly less than the center frequency. For example, a transducer designed to run at 30 kHz will be driven by a generator that sweeps between 29 and 31 kHz. This technology eliminates the standing waves and hot spots in the tank that are characteristic of older, fixed-frequency generators. Auto-follow circuitry is designed to maintain the center frequency when the ultrasonic tank is subjected to varying load conditions. When parts are placed in the tank or when the water level changes, the load on the generator changes. With auto-follow circuitry, the generator matches electrically with the mechanical load, providing optimum output at all times to the ultrasonic tank.
Ultrasonic tanks are generally rectangular and can be manufactured in just about any size. Transducers are usually placed in the bottom or on the sides, or sometimes both when watt density (watts per gallon) is a concern. The transducers can be welded directly into the tank, or watertight immersible units can be placed directly into the aqueous solution. In some instances the immersibles may be mounted at the top of the tank, facing down. For applications such as strip cleaning, one immersible is placed on top and one on the bottom, with minimal distance between them. The strip is then run through the very high energy field. A tank should be sturdy in construction, ranging from 11 to 14 gauge in thickness. Larger, heavy-duty industrial tanks should be 11 to 12 gauge and should contain the proper stiffeners for support due to the weight of the solution.
The solution used in ultrasonic cleaning is a very important consideration. Solvents such as 1,1,1-trichloroethane and freon have been used effectively for many years, with and without ultrasonics. However, with the advent of the Montreal protocol, which calls for elimination of key ozone-depleting substances by 1996, companies are searching for more environmentally friendly methods to clean their parts. Chemical formulators are developing products that meet the demands of cleaning operations, yet are compatible with the health and well-being of society.
Whenever possible, it is best to use a water-based detergent in the ultrasonic cleaning process. Water is an excellent solvent, nontoxic, nonflammable, and environmentally friendly. However, it can be difficult and expensive to dispose of soiled water. Rinsing and drying can also be difficult without detergents. High surface tension exists in solutions without detergents, thus making rinsing difficult in hard-to-reach areas. Detergents can therefore be added to lower the surface tension and provide the necessary wetting action to loosen the bond of a contaminant to a substrate. As an added bonus, the cavitation energy in a water-based solution is more intense than in an organic solvent.
Solution temperature has a profound effect on ultrasonic cleaning effectiveness. In general, higher temperatures will result in higher cavitation intensity and better cleaning. However, if the temperature too closely approaches the boiling point of the solution, the liquid will boil in the negative pressure areas of the sound waves, reducing or eliminating cavitation. Water cavitates most effectively at about 70ºC (160ºF); a caustic/water solution, on the other hand, cleans most effectively at about 82ºC (180ºF) because of the increased effectiveness of the chemicals at the higher temperature. Solvents should be used at temperatures at least 6ºC (10ºF) below their boiling points.
Solution temperature has a profound effect on ultrasonic cleaning effectiveness. In general, higher temperatures will result in higher cavitation intensity and better cleaning. However, if the temperature too closely approaches the boiling point of the solution, the liquid will boil in the negative pressure areas of the sound waves, reducing or eliminating cavitation. Water cavitates most effectively at about 70ºC (160ºF); a caustic/water solution, on the other hand, cleans most effectively at about 82ºC (180ºF) because of the increased effectiveness of the chemicals at the higher temperature. Solvents should be used at temperatures at least 6ºC (10ºF) below their boiling points.
Reprinted with permission from “Ultrasonic Cleaning” by Jeff Hancock, published in the ASM Handbook, Vol. 5, Surface Engineering, p 44-47, copyright 1994, ASM International, Materials Park, OH 44073-0002.